Productname--Ertalon® 6 XAU+*
-
Color--black
-
Average molar mass (average molecular weight)-106 g / mol
-
DensityISO 1183-1g / cm31,150
-
- Water apsorption
-
∙ after 24/96 h immersion in water of 23°C (1)ISO 62mg47 / 89
-
∙ after 24/96 h immersion in water of 23°C (1)ISO 62%0,69 / 1,31
-
∙ at saturation in air of 23°C / 50% RH-%2,2
-
∙ at saturation in water of 23°C-%6,5
-
- Thermal Properties (2)
-
Melting temperature (DSC, 10°C/min)ISO 11357-1/-3°C215
-
Dynamic glass transition temperature +ISO 3146°C
-
Dynamic glass transition temperature ++ISO 3146°C
-
Thermal conductivity Lambda λ at 23°C-W / (K · m)0,290
-
- Coefficient of linear thermal expansion
-
∙ average value between 23 and 60°C-m / (m · K)80 x 10-6
-
∙ average value between 23 and 100°C-m / (m · K)90 x 10-6
-
∙ average value between 23 and 150°C-m / (m · K)
-
- Temperature of deflection under load
-
∙ method A: 1,8 MPaISO 75-1/-2°C80
-
Vicat-Erweichungstemperatur - VST/B50ISO 306°C
-
- Maximal allowable service temperature in air
-
∙ for short periods (3)-°C180
-
∙ continously: for 5.000 / 20.000 h (4)-°C120 / 105
-
Minimal service temperature (5)-°C-30
-
- Flammability (6)
-
∙ Oxygen-IndexISO 4589-1/-2%25
-
∙ according to UL 94 (3 / 6 mm thickness)--HB / HB
-
Specific heat capacity-J / (g · K)1,7
- Mechanical Properties at 23°C (7)
-
- Tension test (8)
-
∙ tensile stress at yield / tensile stress at break (9) +ISO 527-1/-2N / mm284 / -
-
∙ tensile stress at yield / tensile stress at break (9) ++ISO 527-1/-2N / mm255 / -
-
∙ tensile strength (9) +ISO 527-1/-2N / mm286
-
∙ tensile strain at yield (9) +ISO 527-1/-2%5
-
∙ tensile strain at break / elongation at break (9) +ISO 527-1/-2%25 / -
-
∙ tensile strain at break / elongation at break (9) ++ISO 527-1/-2%> 50 / -
-
∙ tensile modulus of elasticity (10) +ISO 527-1/-2N / mm23500
-
∙ tensile modulus of elasticity (10) ++ISO 527-1/-2N / mm21700
-
- Compression test (11)
-
∙ compressive stress at 1/2/5 % nominal strain (12) +ISO 604N / mm226 / 51 / 92
-
- Creep test in tension (8)
-
∙ stress to produce 1% strainISO 899-1N / mm222
-
stress to produce 1% strain (σ 1/1000)ISO 899-1N / mm210,00
-
Charpy impact strenght - Unnotched (12)ISO 179-1/1eUkJ / m2no break
-
Charpy impact strenght - NotchedISO 179-1/1eAkJ / m23,5
-
Charpy impact strength (15° V-notched, both-sided)ISO 11542-2kJ / m2
-
Izod impact strength - Notched +180/2AkJ / m23,5
-
Izod impact strength - Notched ++180/2AkJ / m27,00
-
Ball intentation hardness (13)2039-1N / mm2165
-
Rockwell hardness (134)ISO 2039-2N / mm2M 87
-
Shore hardness D (3 / 15 s)ISO 868N / mm2
-
Coefficient of sliding friction m (14)--0,4 - 0,6
-
Sliding wear method E (14)-µ / km
-
Sliding wear method Q (14)-µ / km11
- Electrical Properties at 23°C
-
Electric strength (15)IEC 60243-1kV / mm29,00
-
Electric strength (15) ++IEC 60243-1kV / mm19,00
-
Volume resistivity +IEC 60093Ω · cm> 1014
-
Volume resistivity ++IEC 60093Ω · cm> 1012
-
Surface resistivity +IEC 60093Ω> 1013
-
Surface resistivity ++IEC 60093Ω> 1012
-
- Relative permittivity ε
-
∙ at 100 Hz +IEC 60250-3,60
-
∙ at 100 Hz ++IEC 60250-6,60
-
∙ at 1 MHz +IEC 60250-3,2
-
∙ at 1 MHz ++IEC 60250-3,70
-
- Dielectric dissipation factor tan Delta δ
-
∙ at 100 Hz +IEC 60250-0,0150
-
∙ at 100 Hz ++IEC 60250-0,1500
-
∙ at 1 MHz +IEC 60250-0,017
-
∙ at 1 MHz ++IEC 60250-0,0500
-
Comparative tracking index (CTI) +IEC 60112-600
-
Comparative tracking index (CTI) ++IEC 60112-600
* Dieser Werkstoff ist ein registriertes Warenzeichen von Mitsubishi Chemical Advanced Materials